<nobr id="hb9dh"><dl id="hb9dh"></dl></nobr>
<output id="hb9dh"><delect id="hb9dh"><font id="hb9dh"></font></delect></output>
    <big id="hb9dh"><listing id="hb9dh"><del id="hb9dh"></del></listing></big>

      <output id="hb9dh"></output>
      <big id="hb9dh"><listing id="hb9dh"><del id="hb9dh"></del></listing></big>

        <nobr id="hb9dh"></nobr>
        <output id="hb9dh"><listing id="hb9dh"><address id="hb9dh"></address></listing></output><nobr id="hb9dh"><delect id="hb9dh"></delect></nobr><output id="hb9dh"><delect id="hb9dh"><pre id="hb9dh"></pre></delect></output>

        <output id="hb9dh"><listing id="hb9dh"><address id="hb9dh"></address></listing></output>

        <menuitem id="hb9dh"></menuitem>
        <output id="hb9dh"></output>
        <video id="hb9dh"><delect id="hb9dh"></delect></video>
        <output id="hb9dh"><delect id="hb9dh"><pre id="hb9dh"></pre></delect></output>

              如何改變湖南鋼纖維的粘結性能
              來源:www.uxdnv.com 發布時間:2022/12/12 14:50:52
                由于鋼纖維與混凝土基體的界面粘結主要是物理性的,即以摩擦剪力的傳遞為主,因此對鋼纖維本身來說,應該從纖維表面和纖維形狀兩個方面來改善其粘結性能。具體的方法有下列四種。
                1。使鋼纖維表面粗糙化、截面呈不規則形。采用熔抽法生產就能達到這個目的。因為鋼纖維在遇空氣急劇冷卻時,表面收縮不均勻而變得粗糙,同時截面也收縮成月牙形,增加與基體的
                接觸面積。

                ⒉沿鋼纖維軸線方向按一定間距對纖維進行塑性加工。例如日本神戶制鋼公司的"信柯"鋼纖維美國雷邦公司的"XOREX"鋼纖維(圖2-1,c)以及慶安鋼鐵廠的"S-2"和"S--3"號鋼纖維。由于表面壓成棱形,或壓成波形,增加了機械粘結力。

              不銹鋼纖維

                ⒊使鋼纖維的兩端異形化。美國貝克爾公甸的"DRAMⅨ"鋼纖維(圖2-1,e)和慶安鋼鐵廠的"S-4‘和as-so型鋼纖維,。都是在兩端制成彎鉤。還有熔抽法抽取的大頭形鋼纖維。由于兩端的錨固作用,提高了抗撥力。

                ⒋對鋼纖維表面涂覆環氧樹脂和表面微銹化處理。這種方法對界面粘結強度的提高不如前幾種方法,但也有一定的效果。

                     湖南雙興鋼纖維有限責任公司憑借先 進的生產技術工藝,專業的檢測設備(牛津儀器以及INNOV-X ALPHA合金分析儀)和完善的管理體系,我公司首 家通過ISO9001國際質量管理體系認證。公司現擁有世界先 進水平的熔抽法、剪切法和冷拔絲全套生產系統,是全球鋼纖維生產設備先 進,產品規格齊全的龍頭企業,具備年產十萬噸的加工生產能力。